COMPARATIVE STUDY ON PROPERTIES OF NANOSTRUCTURED TITANIA SYNTHESIZED BY COLLOIDAL AND POLYMERIC SOLGEL ROUTES
- سال انتشار: 1391
- محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 10، شماره: 1
- کد COI اختصاصی: JR_IJMSEI-10-1_004
- زبان مقاله: انگلیسی
- تعداد مشاهده: 57
نویسندگان
چکیده
Abstract:Nanostructured titania was synthesized by colloidal and polymeric sol-gel routes. Stable colloidal and polymeric titania sols were prepared by adjusting the proper values of the acid/alkoxide and the water/alkoxide molar ratios. The properties of sols were determined by dynamic light scattering technique and synthesized titania was characterized by thermogravimetry and differential thermal analysis, X-ray diffraction, Fourier transform infrared spectroscopy, optical microscopy and field emission scanning electron microscopy. The results showed particle size distribution of colloidal sol ۱۰-۵۰ nm compared to polymeric one which was ۰.۵-۲ nm. Phase analysis of the colloidal sample revealed anatase as the major phase up to ۵۵۰ °C, while the polymeric route resulted only anatase phase up to ۷۵۰ °C. On the basis of results, titania prepared by the polymeric route showed better thermal stability against phase transformation than the sample prepared by the colloidal route. Also, microstructural studies showed that titania nanopowder can be produced by both sol-gel routesکلیدواژه ها
Keywords: Nanostructured Titania; Colloidal sol; Polymeric sol; TiO۲اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.