STUDY OF ANNEALING TEMPERATURE VARIATION ON THE STRUCTURAL PROPERTIES OF DIP-COATED TiO۲-SiO۲ NANOSTRUCTURED FILMS
- سال انتشار: 1391
- محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 10، شماره: 1
- کد COI اختصاصی: JR_IJMSEI-10-1_005
- زبان مقاله: انگلیسی
- تعداد مشاهده: 58
نویسندگان
چکیده
Abstract:In the present research, SiO۲–TiO۲ nanostructure films were successfully prepared on windshields using the sol–gel technique for photocatalytic applications. To prevent the thermal diffusion of the sodium ions from the glass to TiO۲ films, the SiO۲ layer was pre-coated on the glass by the sol–gel method. The substrates were dipped in the sol and withdrawn with the speed of ۶cm/min-۱ to make a gel coating film. The coated films were dried for ۲ days at ۲۷ °C to allow slow solvent evaporation and condensation reactions due to rapid sol–gel reaction of Titania precursor. Then, the films were annealed at ۱۰۰ °C for ۳۰min and at the final temperature (۵۰۰, ۷۰۰ °C) for ۳۰ min continuously. The structure and surface morphology properties, which are as a function of annealing temperature, have been studied by SEM FE-SEM and XRD. The FE-SEM surface morphology results indicate that the particle size increases from ۱۹ to ۴۲ nm by increasing the annealing temperature from ۵۰۰ °C to ۷۰۰ °C. Likewise, XRD illustrate the crystal anatase and rutile as main phases for TiO۲-SiO۲ films annealed at ۵۰۰ °C and ۷۰۰ °C respectively. This procedure resulted in transparent, crack-free SiO۲–TiO۲ films.کلیدواژه ها
Keywords: SiO۲–TiO۲, thin films, sol–gel, dip coatingاطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.