EFFECT OF IMMERSION TIME ON THE ELECTROCHEMICAL BEHAVIOUR OF AISI ۳۲۱ STAINLESS STEEL IN ۰.۱ M H۲SO۴ SOLUTION

سال انتشار: 1393
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 11، شماره: 2
کد COI اختصاصی: JR_IJMSEI-11-2_006
زبان مقاله: انگلیسی
تعداد مشاهده: 43

نویسندگان

Faculty of Engineering, Bu-Ali Sina University, Hamedan, Iran.

چکیده

In this study, effect of immersion time on the electrochemical behaviour of AISI ۳۲۱ stainless steel (AISI ۳۲۱) in ۰.۱ M H ۲SO ۴ solution under open circuit potential (OCP) conditions was evaluated by potentiodynamic polarization, Mott–Schottky analysis and electrochemical impedance spectroscopy (EIS). Mott–Schottky analysis revealed that the passive films behave as n-type and p-type semiconductors at potentials below and above the flat band potential, respectively. Also, Mott–Schottky analysis indicated that the donor and acceptor densities are in the range ۱۰۲۱ cm-۳ and increased with the immersion time. EIS results showed that the best equivalent circuit presents two time constants: The high-medium frequencies time constant can be correlated with the charge transfer process and the low frequencies time constant has been associated with the redox processes taking place in the surface film. According to this equivalent circuit, the polarization resistance (interfacial impedance) initially increases with the immersion time (۱ to ۱۲ h), and then it is observed to decreases. This variation is fully accordance with potentiodynamic polarization results

کلیدواژه ها

Stainless steel, immersion time, Mott–Schottky, Equivalent circuit

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.