Improvement of alignment degree of electrospun nanofibers in rotating jet method
- سال انتشار: 1391
- محل انتشار: چهاردهمین کنگره ملی مهندسی شیمی ایران
- کد COI اختصاصی: NICEC14_597
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1007
نویسندگان
Department of Chemical Engineering, Faculty of Engineering, University of Kurdistan, Sanandaj ۶۶۱۷۷, Iran
چکیده
In this study by exerting a simple modification over the spinneret of rotating-jet electrospinning method, the alignment degree of electrospun fiber was improved. For this propose a layer ofplastic insulation was covered onto the spinneret of the rotating-jet electrospinning method. SO, the effective length of spinneret which controls the strength of electrostatic field was changed. To evaluate the effectiveness of this modification, the obtained results for various spinneret effectivelengths at various voltages were compared with published data. It was revealed that, as theeffective length of spinneret is decreased from 3.2 cm to 0.5 cm the alignment degree is increased more than three times.کلیدواژه ها
Electrospinning; nanofibers alignment; PAN; uniaxial nanofibers; rotating jet methodمقالات مرتبط جدید
- سنتز نانو ماده اکسیدگرافن و بررسی تاثیر آن بر روی مقاومت شیمیایی رنگ آلکیدی
- پیش بینی نرخ های تولید چندفازی (نفت، گاز و آب) با استفاده از روش های یادگیری ماشین: مرور بر روش ها و کاربردها
- روشهای کنترل داده محور در مهندسی شیمی
- بررسی جداسازی گاز پروپیلن از پروپان در غشای ۶FDA-durene با استفاده از روش شبیه سازی مولکولی
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.