Tensile and Flexural Properties of ۳D-Printed Polylactic Acid/Continuous Carbon Fiber Composite
- سال انتشار: 1402
- محل انتشار: مجله مکانیک سازه های پیشرفته کامپوزیت، دوره: 10، شماره: 2
- کد COI اختصاصی: JR_MACS-10-2_016
- زبان مقاله: انگلیسی
- تعداد مشاهده: 192
نویسندگان
Faculty of Mechanical Engineering, Semnan University, Semnan, Iran
Faculty of Mechanical Engineering, Semnan University, Semnan, Iran
Faculty of Mechanical Engineering, Semnan University, Semnan, Iran
چکیده
Fused deposition modeling is one of the most common methods of additive manufacturing that has enabled the ۳D printing of composites. Compared with traditional procedures, this method reduces part cost and production time. This paper investigated the effects of layer height, print speed, and nozzle temperature on the tensile and flexural characteristics of polylactic acid/continuous carbon fiber (PLA/CCF) composite. Two predicting models were developed based on the mechanical tests' data to estimate composite specimens' tensile and flexural strength. These models were used in a two-objective optimization procedure to obtain the composite's highest tensile and flexural strength. The optimum layer thickness, print speed, and nozzle temperature values were ۰.۳ mm, ۴ mm/s, and ۲۰۰°C, respectively. Adjusting the optimal values of the study parameters increased tensile and flexural strength by ۷۷ and ۲۷.۵ percent, respectively, over the unreinforced sample. Furthermore, the fracture section of the composite was examined by scanning electron microscopy (SEM). The SEM images showed that the printing parameters influenced fiber impregnation, which in turn affected the sample's strength. Finally, two composite samples were successfully ۳D printed with higher complexity using the optimized values of the studied parameters.کلیدواژه ها
Additive Manufacturing, Fused Deposition Modeling, Polymer matrix composites, Carbon fiber, Continuous Fiber Compositesاطلاعات بیشتر در مورد COI