Preparation of durable hydrophobic surface using sol-gel method on cellulosic fabric

سال انتشار: 1402
محل انتشار: دوازدهمین کنفرانس بین المللی فناوری های نوآورانه در زمینه علوم ، مهندسی و تکنولوژی
کد COI اختصاصی: TETSCONF12_017
زبان مقاله: انگلیسی
تعداد مشاهده: 330

نویسندگان

Department of Polymer Engineering and Color Technology, Amirkabir University of Technology, Tehran, Iran

Colour and Polymer Research Centre, Amirkabir University of Technology (Polytechnic), P. O. Box ۱۵۸۷۵-۴۴۱۳, Tehran, Iran

چکیده

A low temperature process of superhydrophobic finishing of cotton fabric has been developed by sol gel method. Cellulose fabric was first coated with silica sol and butane tetracarboxylic acid (BTCA) as the acidic catalyst. The silica coated fabric was then padded with hydrolyzed alkyl silane afterwards obtaining low surface energy. Water contact angle was used to characterize superhydrophobicity. Scanning electron microscopy was used to see the surface of coated fabrics. Contact angle (CA) reached to ۱۵۸ degree and with washing CA decreased slightly. BTCA formed the ester bonds between cotton fabric and silica sol and improved the durability of superhydrophobicity.

کلیدواژه ها

Super hydrophobic, sol gel, cellulosic fabric, polycarboxylic acid

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.