بررسی دگرگونی فاز و ساختار منطقه متاثر حرارتی شبیه سازی شده جوش دوپاسه در فولاد میکروآلیاژ X۷۰
- سال انتشار: 1401
- محل انتشار: دوفصلنامه علوم و فناوری جوشکاری ایران، دوره: 8، شماره: 2
- کد COI اختصاصی: JR_JWSTI-8-2_019
- زبان مقاله: فارسی
- تعداد مشاهده: 112
نویسندگان
Department of Materials Engineering, Saveh Branch, Islamic Azad University, Saveh, Iran.
چکیده
In multi-pass welding, the heat-affected zone formed in each pass is subjected to another thermal cycle by the next pass. This problem locally changes the microstructure of the heat-affected zone depending on the position of each area relative to the melting line of the next pass, and the overlapping of the heat-affected areas will lead to complex microstructures. In this research, based on the practical conditions of pipe production in the factory, including submerged arc welding with four electrodes in two passes from the inside and outside of the pipe, the thermal cycles of the heat-affected zone were first analyzed. Simulation of thermal cycles of heating and cooling up to the peak temperatures of ۹۵۰, ۱۱۵۰ and ۱۳۵۰ °C was performed in a dilatometer and the transformation behavior and microscopic structure were studied. Simultaneous modeling of precipitation dissolution and austenite grain growth was done. It was observed that the grain growth reaches a limit in ۳۰۰ seconds. The main cause of grain growth at temperatures below and above ۱۱۵۰ °C, is the dissolution of fine and coarse deposits of niobium carbonitride, respectively. Also, the modeling of austenite formation and decomposition was done using the classic JMAK equation. It was observed that the parameter n does not depend much on temperature; while parameter k strongly depends on temperature, transformation amount and austenite grain size.کلیدواژه ها
pipeline steel, submerge arc welding, dilatometry, phase transformation, heat affected zone, فولاد خط لوله, جوشکاری زیرپودری, دیلاتومتری, دگرگونی فاز, منطقه متاثر حرارتیاطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.