Preparation of polyaniline composite electrode by in-situ electropolymerization forapplication in supercapacitors
- سال انتشار: 1401
- محل انتشار: هفدهمین سمینار سالانه الکتروشیمی ایران و دوازدهمین کنفرانس پیل سوختی ایران
- کد COI اختصاصی: ELECTROCHEMISTRY017_094
- زبان مقاله: انگلیسی
- تعداد مشاهده: 118
نویسندگان
Chemistry Department, Faculty of Science, University of Guilan, , Rasht, IranP.O. Box: ۱۹۱۴–۴۱۳۳۵
Chemistry Department, Faculty of Science, University of Guilan, , Rasht, IranP.O. Box: ۱۹۱۴–۴۱۳۳۵
Chemistry Department, Faculty of Science, University of Guilan, , Rasht, IranP.O. Box: ۱۹۱۴–۴۱۳۳۵
چکیده
In recent years, supercapacitors have attracted significant attention due to the fastcharging/discharging rate, high power density, and long cycle life provide a viable solution toaddress the increasing demand. In the following study, the CoS۲/polyaniline (PANI) electrodegrown on nickel foam (NF) have been successfully constructed through a facile method and usedas electrodes for a high-performance pseudo capacitor. Firstly, CoS۲ salt was fabricated onto nickelfoam (NF) by a hydrothermal method. Then, PANI was formed in situ on the surface of the CoS۲via an electropolymerization route to achieve high specific capacitance, and long-term life forrequired supercapacitor electrode applications. The electrochemical properties of theseCoS۲/PANI/NF electrodes were studied using cyclic voltammetry (CV), galvanostatic chargedischargeanalysis (GCD), and electrochemical impedance spectroscopy (EIS) techniques. Thehighest specific capacitance obtained by the prepared electrode was ۲۴۴۳.۳۳ F g –۱ at a currentdensity of ۱ A g –۱, and ۹۳.۰۴% specific capacitance retention after ۳۰۰۰ charge/discharge cyclesat a current density value of ۸ A g –۱. Moreover, a supercapacitor was fabricated using CoS۲/PANIon NF as the positive electrode (cathode), and activated carbon on Ni foam (AC/NF) as thenegative electrode (anode) exhibited high specific capacitance of ۱۴۸.۵ F g –۱ at a current densityof ۱ A g –۱. The introduced composite electrode based on PANI in this research showed excellentelectrochemical performances to be used as electrode material in supercapacitors as novel energystorage devices.کلیدواژه ها
Energy storage, Supercapacitor, Hydrothermal method, Polyaniline, cobalt disulfideمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.