effect of vauum brazing cycles on wetting angel and microstructure of Bni-2 BRAzing alloy joining
- سال انتشار: 1388
- محل انتشار: کنگره بین المللی جوش و روشهای اتصال
- کد COI اختصاصی: IIWC01_074
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1163
نویسندگان
university of tehran
چکیده
surface wetting of base metals by brazing alloys is one of the mostimportant effective parameter in joining by brazing since in this investigation vacuum brazing process using BNI-2 brazing alloy was applied for these types of joints brazing cycles were performed at temperatures ranging from 1020 to 1050 C under different holding times ranging from 5 to 20 minutes acoording to classical model surface wetting angel was measured by light microscope it was observed that wetting angel is decreased by increasing temperature or time in brazing cycles . micriostructure and chemical composition of solidified brazing alloy was evaluated by scanning electron microscope SEM equipped with an energy dispersive spectroscopy EDS UNIT. the results showed that tehre are three different zones in the solidified brazing alloys.کلیدواژه ها
brazing,brazing alloy,wetting angelمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.