the influence of welding speed on microhardness and microstructure in dissimilar friction stir welded of AA6061-T6 and AA7071-T6
محل انتشار: کنگره بین المللی جوش و روشهای اتصال
سال انتشار: 1388
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,315
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IIWC01_024
تاریخ نمایه سازی: 6 مهر 1391
چکیده مقاله:
int this research the effect of welding speed on the properties of the weld such as the microhardness distribution and the grain size at the stir zone of the joints produced by the friction stir welding between AA7075-T6and AA6061-T6 alloys has been investigated the microhardness variations were determined for different welding speeds during FSW process the peak temperatures were measured for determining the relationship between the peak temperature and the hardness distribution at HAZ. beside the microstructure analysis was performed for evaluaing the influence of welding speed on the developed grain size.
کلیدواژه ها:
نویسندگان
p bahemmat
iran university of science &tech
m.k besharati givi
university of tehran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :