The Effect of the Cu Concentration on the Magnetic Properties and Microstructure of the Electrodeposited CoCu Nanowires

سال انتشار: 1387
محل انتشار: دومین کنگره بین المللی علوم و فناوری نانو
کد COI اختصاصی: ICNN02_630
زبان مقاله: انگلیسی
تعداد مشاهده: 957

نویسندگان

Institute of Nanoscience and Nanotechnology, University of Kashan, Kashan, Iran

چکیده

Perpendicular magnetic recording system is one of the most promising candidates to realize the extremely high-density recording (HDR) due to its superior thermal stability and high track density [1]. One such technology to prepare sample with high perpendicular magnetic anisotropy is based on nanowires. Different techniques have been employed to fabricate nanowires . Among them, the template method has proved to be a simple and versatile approach. Electrodepositing the magnetic metal wires with nanoscale into the porous anodic aluminum oxide (AAO)templates have been utilized previously by many groups to prepare the one-dimensional nanostructure[2]. Recently, ferromagnetic-nonmagnetic alloy systems have attracted much interest[3]. Examples of such nanostructures are magnetic Co/Cu multilayers exhibiting giant magnetoresistance (GMR)[4] . A coercivity of 278, 244 and 238 Oe is reported for Co0.77Cu0.23 nanowires with 20, 30 and 40 nm, diameter, respectively [5]. In the present work, we fabricated CoCu nanowires by pulse electrodeposition of ions into PAO templates, using different composition. The magnetic properties and microstructures of composition have been investigated.

کلیدواژه ها

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.