Effect of Additive and Rapid Solidification Rate on Magnetic Properties of an Amorphous Co-based Alloy
- سال انتشار: 1387
- محل انتشار: دومین کنگره بین المللی علوم و فناوری نانو
- کد COI اختصاصی: ICNN02_233
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1153
نویسندگان
Ms.C student of Department of Materials engineering, Azad University of Saveh
Asistant Professor of Department of Materials engineering, Azad University of Saveh, Saveh
Maham Industries
چکیده
Investigations on soft magnetic materials are performed to increase magnetic permeability, magnetization saturation and to decrease coercivity. Due to no crystalline microstructure at amorphous materials, magnetocrystaline anisotropy of them is so low and their permeability is so high, but there are industrial needs to increase permeability more [1,2]. Increasing of permeability is guaranteed at amorphous materials but decreasing of magnetization is happened in these systems too. Additional elements can help to get optimizedmagnetic properties. There is not any exact idea to answer how additional elements effect on ultimate magnetic properties [3-5]. Co-base amorphous alloys have maximum permeability in soft magnetic materials. In this work, synthesizing of amorphous soft magnetic ribbons Co64Fe4Ni2B19-xSi8Cr3Alx (x=0, 1, 2, 3) by melt spinning method is studied and optimized Al amount in this alloy with the best magnetic properties is determined.کلیدواژه ها
مقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.