A novel coating process for preparation of ZnO nanostructure thin film on glass beads

سال انتشار: 1387
محل انتشار: دومین کنگره بین المللی علوم و فناوری نانو
کد COI اختصاصی: ICNN02_141
زبان مقاله: انگلیسی
تعداد مشاهده: 1613

نویسندگان

Catalysis Division, Department of Chemistry, University of Isfahan, Isfahan

چکیده

ZnO was deposited onto glass beads (diameter 5mm) substrate by our novel centrifuge coating technique using sol-gel method. Glass beads were etched, covered with sol and placed in a centrifuge tube with 4000 rpm for 90 seconds. They were subsequently pre-heated at 275 0C for 5 min, and post-heated at 550 0C for 1 hour. The morphologies, phase structure and the optical properties of the thin films were investigated by scanning electron microscopy (SEM), X-ray diffractometer (XRD). ZnO nano-sized particles show an average diameter about of 40 nm. X-ray diffraction results showed polycrystalline wurtzite with a c-axis preferential (002) orientation with the sharp X-ray diffraction peak at 34.40 corresponding to the hexagonal ZnO. These sol-gel deposited ZnO films on glass beads have potential application as transparent electrodes in optic and electronic devices and immobilized catalyst

کلیدواژه ها

Nanostructure; sol-gel; thin films; glass bead; coatings

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.