Siliconization of Molybdenum using glow discharge method
- سال انتشار: 1402
- محل انتشار: مجله تحقیقات و کاربردهای هسته ای، دوره: 3، شماره: 1
- کد COI اختصاصی: JR_JORNA-3-1_003
- زبان مقاله: انگلیسی
- تعداد مشاهده: 148
نویسندگان
Department of Biotechnology, Persian Gulf Research Studies Center, Persian Gulf University, ۷۵۱۶۹, Bushehr, Iran
Nuclear Energy Research Centre, Physics Department, Persian Gulf University, Bushehr, P. O. Box: ۷۵۱۶۹, Iran
Medical Radiation Research Center, Central Tehran Branch, Islamic Azad University, Tehran, Iran.
چکیده
The thin layer of Silicon film has been deposited on molybdenum samples at room temperature for the first time by a mixture of silane and He gas (۹۰ % He+۱۰ % SiH۴) using the glow discharge method as an application of a low -Z protective material to a fusion reactor. Siliconization has been conducted for ۱۷۰ min with the gas pressure of ۴–۶ ×۱۰-۲ torr. the DC power supply parameters were as follows, the anode voltage of ۵۰۰–۶۰۰ V, and the current of ۱۹۰-۲۱۰ mA. The films have been characterized by using scanning electron microscopy, EDX, X-ray diffraction, FTIR, and AFM. SEM images show that the silicon coating covers the entire surface smoothly and there is no boundary for granulation. The thickness of the coating has been estimated to be around ۴۵۰ nm using AFM measurement. The Si-O-Si tensile vibrations and Si-H tensile vibrations have been detected using FTIR method.کلیدواژه ها
low Z material, Molybdenum, Silicon coating, Glow Dischargeاطلاعات بیشتر در مورد COI