Effect of Mechanical Activation on the Kinetics of Ammoniacal Thiosulfate Leaching of a Refractory Oxide Gold Ore

سال انتشار: 1398
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 16، شماره: 2
کد COI اختصاصی: JR_IJMSEI-16-2_007
زبان مقاله: انگلیسی
تعداد مشاهده: 270

نویسندگان

Hamedan University of Technology

چکیده

The effect of mechanical activation on the kinetics of ammoniacal thiosulfate leaching of a refractory oxide gold ore containing ۲.۸ ppm Au was investigated. The gold extraction of ۹۹.۸۱% was achieved by ۱۶ h leaching of a sample mechanically activated for ۶۰ minutes. The gold extraction observed for a similar reference sample without mechanical activation was only ۵۵%. Studies revealed that leaching progresses at two different rates depending on the leaching time (۰-۲ h and ۲-۱۶ h). It was observed that diffusion through an ash layer as a dominant mechanism controls the leaching of samples mechanically activated up to ۴۵ minutes during total leaching time, while reaction control and liquid film diffusion are dominant mechanisms for leaching of a sample mechanically activated for ۶۰ minutes during ۰-۲ h and ۲-۱۶ h, respectively. The extraction observed during the ash diffusion step depends significantly upon mechanical activation time. Mechanical activation of ۶۰ minutes results in high gold extraction in this step which when combined with subsequent chemical reaction gives close to ۱۰۰% gold extraction in a ۱۶ hour leach. Mechanical activation for up to ۴۵ minutes leads to a modest improvement in overall gold extraction compared with the reference test without mechanical activation

کلیدواژه ها

Kinetics, Mechanical activation, Thiosulfate leaching, Refractory gold ore.

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.