Effect of Heat Treatment on the Microstructure and Soft Magnetic Properties of the Amorphous Fe-B-P-Cu Alloy
- سال انتشار: 1398
- محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 16، شماره: 3
- کد COI اختصاصی: JR_IJMSEI-16-3_001
- زبان مقاله: انگلیسی
- تعداد مشاهده: 216
نویسندگان
School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST)
School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST)
School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST)
Institute of Physics, Częstochowa University of Technology
INRIM, Electromagnetism Division
چکیده
In the present research, rapidly solidified Fe۸۵.۳B۱۱P۳Cu۰.۷ ribbons were prepared by melt spinning process. The microstructural variation as well as magnetic properties of the as-spun and annealed ribbons were characterized by X-ray diffraction (XRD), transmission Mossbauer spectroscopy and alternating gradient field magnetometer (AGFM). The results show two separated distinct exothermic peaks during heating resulting from the phase transition from amorphous to α-Fe and then to Fe۳B, respectively. The study of magnetic properties in the amorphous and nanocrystalline states revealed that annealing the amorphous ribbons at ۴۴۰˚C for ۱۰ minutes gives rise to a significant increase in saturation magnetization (۲۲۰ emu/g) which makes this alloy a good candidate for power applications.کلیدواژه ها
Melt spinning, Mossbauer spectroscopy, Crystallization, Soft magnetic propertiesاطلاعات بیشتر در مورد COI