The effect of the presence of bubbles inside resin on the tensile strength of composites manufactured by vacuum infusion process

  • سال انتشار: 1401
  • محل انتشار: هشتمین کنفرانس بین المللی مواد کامپوزیتی: ساخت، خواص و کاربرد
  • کد COI اختصاصی: COMPOSIT08_068
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 131
دانلود فایل این مقاله

نویسندگان

H Sajedi

Manager, Composite Materials Lab, Department of Mechanical Engineering, Amirkabir University of Technology, Tehran,Iran

M Sadighi

Professor, Department of Mechanical Engineering, Amirkabir University of Technology, Tehran, Iran

K Jafari Khalafloo

Master Graduate, Department of Mechanical Engineering, Amirkabir University of Technology, Tehran, Iran

Reza Hedayati

Post-doctoral researcher, Department of Mechanical Engineering, Amirkabir University of Technology, Tehran, Iran

چکیده

The presence of voids in the structure of composites is one of the important manufacturing defects which hasan undesirable effect on the quality of the composite parts. One of reasons the voids appear in a composite plate is thepresence of bubbles in the resin before it is infused. In this research, the effect of bubbles in the resin and degassingbefore the infusion process on the strength of the glass fiber composites is investigated. Four samples infused by a resinwith bubble to resin ratios of ۲%, ۳%, ۴% and ۵%, and two samples manufactured with degassed and non-degassed resin.The composites were cut and tested according to the ASTM D۳۰۳۹. The results showed that non-degassing and thepresence of bubbles decreases the strength of samples from ۴ to ۲۱.۷%. More specifically, each ۱% increase in thevolume of bubbles decreases the final strength of the composite obtained from the tensile test by ۴.۱% in average.

کلیدواژه ها

Bubbles; Vacuum infusion process; Void defect; Tensile strength

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.