Structural, Morphological and Anti-bacterial Analysis of Nanohydroxyapatite Derived from Biogenic (SHELL) and Chemical Source: Formation of Apatite
- سال انتشار: 1399
- محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 18، شماره: 1
- کد COI اختصاصی: JR_IJMSEI-18-1_010
- زبان مقاله: انگلیسی
- تعداد مشاهده: 144
نویسندگان
Department of Physics, Thiruvalluvar College of Engineering and Technology, Vandavasi – ۶۰۴ ۵۰۵, Tamilnadu, India
Department of Physics, Arunai Engineering College, Tiruvannamalai – ۶۰۶ ۶۰۳, Tamilnadu, India
Ramasamy Mariappan Vimalathithan
Department of Physics, Salem Sowdeswari College (Govt. Aided), Salem – ۶۳۶ ۰۱۰, Tamilnadu, India
Chemistry Divisions, School of Advanced Sciences, Vellore Institute of Technology Chennai campus, VIT University, Chennai-۶۰۰۱۲۷, Tamilnadu, India
Department of Physics, Aarupadai Veedu Institute of Technology, Vinayaka Mission’s Research Foundation, Chennai – ۶۰۳ ۱۰۴, Tamilnadu, India
چکیده
The Nano Hydroxyapatite (HAp), HAp/PEG and HAp/PVP powders derived from both Gastropod shell (natural source) and chemical precursor by the precipitation method were characterized through various characterization techniques such as FT-IR, XRD, SEM-EDX, TEM, Antibacterial activity and SBF analysis. Based on the structural, chemical, morphological and biological characteristics, HAp/PVP from natural and chemical precursors have been compared successfully. Calculated structural parameters, crystallinity index, C/P ratio, morphology, antibacterial activity and SBF analysis of the products show that HAp/PVP-S (derived from a natural source) exhibits good mechanical property, rod like morphology, good antibacterial activity and apatite formation ability at ۱۴ days. EDX analysis also shows the presence of carbon and sodium in HAp/PVP-S. Comparative analysis reveals that characteristics of HAp/PVP-S such as high carbonate content, low crystallite size, poor crystalline nature, presence of trace metal, non-stoichiometric elemental composition and rod like crystals which are matched with the characteristics of biological apatite. Thus, the HAp/PVP-S has the ability to form bone apatite.کلیدواژه ها
Hydroxyapatite, Precipitation Method, Comparative Analysis, Antibacterial activity, SBF Analysisاطلاعات بیشتر در مورد COI