Effect of Solution Treatment on the Rollability of a Cu-Ni-Mn-Sn Alloy
- سال انتشار: 1400
- محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 19، شماره: 1
- کد COI اختصاصی: JR_IJMSEI-19-1_007
- زبان مقاله: انگلیسی
- تعداد مشاهده: 202
نویسندگان
Materials Engineering Group, Golpayegan College of Engineering, Isfahan University of Technology, ۸۷۷۱۷-۶۷۴۹۸, Golpayegan, Iran
Department of Metallurgy and Materials Engineering, Hamedan University of Technology, Hamedan,Iran
Department of Materials Engineering, Malek-Ashtar University of Technology, ۱۶۷۸۸-۱۵۶۱۱, Iran
Department of Materials Engineering, Malek-Ashtar University of Technology, ۱۶۷۸۸-۱۵۶۱۱, Iran
Materials Engineering Group, Golpayegan College of Engineering, Isfahan University of Technology, ۸۷۷۱۷-۶۷۴۹۸, Golpayegan, Iran
چکیده
In this research, the effect of initial microstructure and solution treatment on rollability and crystallographic texture of a Cu-Mn-Ni-Sn alloy has been investigated. The initial tests indicated that the rolling of the alloy at different temperature conditions is not possible due to formation of second phases. Herein to eliminate the segregated phases, according to DTA analysis, proper temperature for solution treatment was selected as ۷۵۰°C applied at different periods of time. The obtained results showed that after ۱۵-hour solution treatment, the complete elimination of Sn, Mn, Ni, and Fe-rich phases can be achieved. Also, the peaks of XRD shifted to the higher angles indicating that the alloying elements are dissolved. Meanwhile, the intensity of the texture reduced and the dominant texture changed from Goss and Brass-texture to Copper-texture. Accordingly, the amount of maximum total reduction at the rolling process increased from ۱۶.۳۷ to ۱۰۹.۴۶ after solution treatment.کلیدواژه ها
Microstructure, Texture, X-ray diffraction (XRD), rollability, Solution treatmentاطلاعات بیشتر در مورد COI