Modify thermoelectric properties of ZnO with ZrO2 nanoparticles additive
- سال انتشار: 1390
- محل انتشار: پنجمین کنفرانس بین المللی پیشرفت های علوم و تکنولوژی
- کد COI اختصاصی: SASTECH05_218
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1264
نویسندگان
Department of Materials Science Engineering, School of Engineering, , Shiraz University
Professor in Materials Science Engineering, Department of Materials Science Engineering, School ofShiraz University,
چکیده
Solid-state reaction processing technique was used to prepare ZnO-doped ZrO2 samples. The XRD patterns of the samples showed that Zr4+ ions substituted Zn2+ ions in the Zinc oxide structure. The SEM results revealed that the grain size of the Zinc oxide decreases with increasing ZrO2 content. Thermoelectric measurements show that the addition of ZrO2 to ZnO led to a significant increase in the electrical conductivity and a decrease in the absolute value of the Seebeck coefficient. Significant reduction of the thermal conductivity was observed as compared to pure ZnO sample. The figure of merit ZT values of Zno-doped ZrO2 samples are higher than the ZnO pure sample, specially at high temperatures , this demonstrated that the ZrO2 addition is fairly effective for enhancing thermoelectric propertiesکلیدواژه ها
Thermoelectric; Zinc oxide; Thermal conductivity; Electrical conductivity; Seebeck coefficient; Figure of meritمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.