Role of Ti۳AlC۲ MAX phase on characteristics of in-situ synthesized TiAl intermetallics. Part II: phase evolution

  • سال انتشار: 1400
  • محل انتشار: فصلنامه سنتز و تفجوشی، دوره: 1، شماره: 4
  • کد COI اختصاصی: JR_SYNSINT-1-4_003
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 267
دانلود فایل این مقاله

نویسندگان

Maryam Akhlaghi

Semiconductors Department, Materials and Energy Research Center (MERC), Karaj, Iran

Esmaeil Salahi

Ceramics Department, Materials and Energy Research Center (MERC), Karaj, Iran

Seyed Ali Tayebifard

Semiconductors Department, Materials and Energy Research Center (MERC), Karaj, Iran

Gert Schmidt

Faculty of Mechanical, Process and Energy Engineering, TU Bergakademie, Freiberg, Germany

چکیده

In this research, the ۲nd part of a series of papers on the processing and characterization of TiAl–Ti۳AlC۲ composites, the phase evolution during the manufacturing process was investigated by X-ray diffraction (XRD) analysis and Rietveld refinement method. Metallic Ti and Al powders with different amounts of previously-synthesized Ti۳AlC۲ additives (۱۰, ۱۵, ۲۰, ۲۵ and ۳۰ wt%) were ball-milled and densified by spark plasma sintering (SPS) under ۴۰ MPa for ۷ min at ۹۰۰ °C. Before the sintering process, XRD test verified that the powder mixtures contained metallic Ti and Al as well as Ti۳AlC۲ and TiC (lateral phase synthesized with Ti۳AlC۲) phases. In the sintered composites, the in-situ synthesis of TiAl and Ti۳Al intermetallics as well as the presence of Ti۳AlC۲ and the formation and Ti۲AlC MAX phases were disclosed. The weight percentage of each phase in the final composition of the samples and the crystallite size of different phases were calculated by the Rietveld refinement method based on the XRD patterns. The size of Ti۳AlC۲ crystallites in sintered samples was compared with the crystallite size of synthesized Ti۳AlC۲ powder.

کلیدواژه ها

Spark plasma sintering, TiAl, Ti۳AlC۲, Phase analysis, Rietveld refinement, Crystallite

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.