Fabrication of High Luminescent Mn Doped CdS Semiconductor Nanoparticles

سال انتشار: 1391
محل انتشار: بیستمین کنفرانس مهندسی برق ایران
کد COI اختصاصی: ICEE20_097
زبان مقاله: انگلیسی
تعداد مشاهده: 1335

نویسندگان

Faculty of New Sciences & Technologies, University of Tehran, P.O.BOX:۱۴۳۹۵-۱۵۶۱, Tehran, Iran

Department of Electrical Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran

چکیده

In this work we have synthesized bare and doped CdS nanoparticles and studied luminescence properties of these particles as an important II-VI semiconductor. Thethermochemical method is used for synthesis of these nanoparticles. Thiols are usually used as the capping agent to prevent further growth. Na2S2O3 was used as the sulfurprecursor, 3CdSO4.8H2O as the Cadmium precursor, Thioglycolic acid (TGA) as capping agent and Mn(NO3)2.4H2Oas Manganese doping precursor in thermochemical and room temperature growth. The application of TGA as capping agentinstead of TG was studied as a novel idea in this research and was used practically in the synthesis of semiconductor nanoparticles. Using this process resulted in particles with sizesbetween 3-7nm. Several samples were synthesized and characterized under various conditions such as variation of Mnions doping ratio, different temperatures, and different TGA concentrations. Synthesis of CdS nanoparticles with large Mn ions concentration resulted in decrement of their luminescence. In other words luminescence of nanoparticles was increased bydecreasing Mn:Cd doping ratio. In this work synthesized nanoparticles under different doping ratios, and two samples which had the best results were Mn:Cd=1:80 andMn:Cd=1:160 respectively. The particles growth under various temperatures indicated that decreasing temperature resulted in small particles, but their luminescence intensity fell downbecause of dominance of Mn emission in low temperatures. Also the results of particles growth under various TGAconcentrations indicate the decrement of particles size distribution with increase of TGA concentration.

کلیدواژه ها

CdS semiconductor nanoparticles, thermochemical growth, luminescence

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.