The effect of O2/H2 gas ratio of post-oxidation treatment on corrosion behaviour of plasma nitrided AISI 316 austenitic Stainless Steel
- سال انتشار: 1391
- محل انتشار: سومین کنفرانس بین المللی عملیات حرارتی مواد
- کد COI اختصاصی: ICMH03_070
- زبان مقاله: انگلیسی
- تعداد مشاهده: 2176
نویسندگان
Department of Materials Engineering, Islamic Azad University , Najafabad Branch, Isfahan, Iran
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
Department of Materials Engineering, Islamic Azad University , Najafabad Branch, Isfahan, Iran
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
چکیده
In this research, the microstructure and corrosion properties of plasma nitriding and post oxidation treated AISI 316 austenitic stainless steel have been studied. Plasma nitriding was carried out at 450 °C for 5 hr in a D.C plasma with gas mixture of 25% N2- 75% H2 followed by post-oxidation process in gas mixtures of O2/H2: 1/3, 1/5, 1/9 and 1/12 for 30 min. The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical polarization readings. The results showed that the plasma nitriding decreases the corrosion resistance of the steel substrate. However, post-oxidizing treatment improves both uniform and pitting corrosion resistances of the nitrided specimens. This effect was most pronounced by post-oxidizing treatment at lower O2/H2 ratios due to the development of magnetite as a more dense oxide phaseکلیدواژه ها
plasma nitriding, stainless steel, corrosion, post- oxidationمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.