Influence of Heat Treatment Assisted by Pressure on Mechanical Properties of Al2O3-SiC Nanocomposites
- سال انتشار: 1391
- محل انتشار: سومین کنفرانس بین المللی عملیات حرارتی مواد
- کد COI اختصاصی: ICMH03_060
- زبان مقاله: انگلیسی
- تعداد مشاهده: 2180
نویسندگان
Faculty of Materials Engineering, Malek ashtar University of Technology, Tehran, Iran
Faculty of Materials Engineering, Malek ashtar University of Technology, Tehran, Iran
Faculty of Materials Engineering, Malek ashtar University of Technology, Tehran, Iran
چکیده
Al2O3-SiC composite is difficult to sinter to full density. The densification method for these composites is therefore hot pressing. In this study, the effect of hot pressing temperature on mechanical properties of Al2O3 based nanocomposite containing 10 vol. % nano-SiC and nano-MgO particles was investigated. The hot pressing was carried out at 1600°C to 1750°C temperatures at 30 MPa pressure. SEM and density results appear that increasing ofhotpressing temperature increased density and particle size of grains. Also as sintering temperature was increased, flexural strength to 396 MPa, hardness to 19.5 GPa, and toughness fracture to 3.6 MPa.m1/2 were improvedکلیدواژه ها
hot pressing, nanocomposites, alumina; silicon carbide, Mechanical Propertiesمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.