The effects of heat treatment on the mechanical properties of wear resistant Cr-Mo Steel

  • سال انتشار: 1391
  • محل انتشار: سومین کنفرانس بین المللی عملیات حرارتی مواد
  • کد COI اختصاصی: ICMH03_054
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 2100
دانلود فایل این مقاله

نویسندگان

Mahyar Mohammadnezhad

Research and Development Unit of Isfahan Casting Industres (ICI)

Vahid Javaheri

Department of Materials Engineering,Iran University of Industries & Mines

چکیده

The effects of heat treatment on the properties of wear-resistant Fe-0.7C-2.3Cr-0.4Mo-0.5Si alloy steel which is used to make the liner of rolling mill were researched. The results show that when quenching temperature is lower than 940 °C , the hardness increases with the increase of temperature, and when quenching temperature is higher than 960 °C , the hardness decreases with the increase of temperature. As quenching temperature is lower than 940 °C , the effect of quenching temperature on the impact toughness is not obvious. When quenching temperature is higher than 960 °C, impact toughness decreases with the increase of temperature. When tempering temperature is higher than 400 °C , the hardness begins to decrease obviously. After tempering at 300 °C , the best wear resistance was obtained. According to the service condition of rolling mill liner, the Cr-Mo Steel is quenched from 940-960 °C and tempered at 300-320 °C.

کلیدواژه ها

heat treatment, wear resistant, mechanical properties, liner

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.