Effect of annealing on microstructure and corrosion properties of Admiralty brass alloy tube in 3.5% NaCl solution
- سال انتشار: 1391
- محل انتشار: سومین کنفرانس بین المللی عملیات حرارتی مواد
- کد COI اختصاصی: ICMH03_050
- زبان مقاله: انگلیسی
- تعداد مشاهده: 2323
نویسندگان
چکیده
The microstructure and corrosion resistance of annealed Admiralty brass alloy tube were investigated using optical microscope, X-ray diffraction (XRD), DC polarization measurements and electrochemical impedance spectroscopy (EIS), respectively. The recrystallizations gradually increased with the increase of annealing temperature and holding time. As annealing temperature and holding time increase, corrosion potential (EC) increased while corrosion rate (iC) decreased at 3.5% NaCl solution. The impedance measurements have shown that the corrosion rate of the alloy decreases with the immersion time from 0 to 15 days. The SnO2 surface film and the Sn-rich phases were responsible for the corrosion resistance of annealed Admiralty brass alloy tube in 3.5 wt. % NaCl solution. It was found that the Admiralty brass alloy tube annealed at 780°C for 120 min exhibited favorable corrosion resistanceکلیدواژه ها
Admiralty brass alloy tube, Annealing, Microstructure, corrosion resistanceمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.