A study on aluminum matrix composite reinforced with a two-dimensional network of interconnected steel wires fabricated by lost foam casting
- سال انتشار: 1391
- محل انتشار: اولین کنفرانس بین المللی مواد پیشرفته
- کد COI اختصاصی: NAMIC01_106
- زبان مقاله: انگلیسی
- تعداد مشاهده: 2041
نویسندگان
Department of Materials and Metallurgical Engineering, Iran University of Science and Technology (IUST
Associate Professor
Associate Professor
چکیده
The current investigation involves fabrication and characterization of aluminum alloy (A356) matrix composites reinforced with the interconnected, twodimensional, steel wire performs. The composites were produced by lost foam casting process and wereheat treated to get ‘reaction interface’ (RI). Micro hardness and tensile properties of the matrix, as-cast and heat treated composites have been determined and the microstructure of the specimens was examined with optical and scanning electron microscopes. Micro structural characterization conducted on the as-cast composite samples showed some pores at the Al matrix/steel wire interface. However, nearly all the heat treated composites showed a completed bonding because of the formation of reaction layer at the interface. Hardness and strength of composites increased as compared to matrix alloy. The mechanical properties of these composites were measured and the results were correlated with the microstructure observation. While micro hardness of the composite showed variation from 150 to 56 Hv across the interface in the as-cast composite, annealed (450-525°C) composite showed a micro hardness of 810-960 Hv at the interface indicating the effectiveness of the heat treatment. The results have been discussed in terms of wetting between steel wires and the matrix, particularly the increase of hardness and tensile strength to the formation of ‘reaction interface’ due to annealing. The width of the interface increased with annealing time and temperature.کلیدواژه ها
Aluminum matrix composites, Reaction interface, Annealing, Mechanical properties, Lost foam castingمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.