The Effects of V and Cr Addition on the Deformation Mechanisms and Mechanical Behavior of a Binary TiAl Alloy
- سال انتشار: 1391
- محل انتشار: اولین کنفرانس بین المللی مواد پیشرفته
- کد COI اختصاصی: NAMIC01_091
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1628
نویسندگان
Department of Materials and Metallurgical Engineering, Iran University of Science and Technology, Tehran, Iran
Department of Materials and Metallurgical Engineering, Iran University of Science and Technology
Department of Mechanical Engineering, Ecole de Technologie Superieure, Montreal, Canada
چکیده
In the present study, to determine the influence of the Vanadium and Chromium additions on the deformation mechanisms of the TiAl based alloys, theoretical and experimental approaches were used. In one hand, the changes of electronic structure parameters in the lattice of ternary TiAl alloys were calculated by employing the discrete variational Xα cluster method. Calculations were set such to consider the ternary TiAl containing third alloying elements for about 2 at.% in the hypothetical composition. Parameters changes of the bond strength, the bonding anisotropy ratio and the lattice resistivity to the micro-deformations, by addition of V and Cr alloying elements were calculated and discussed. In the other hand, experimental tension tests were designed and carried out at ambient temperature on the standard samples of the Ti-48Al, Ti-48Al-2V and Ti-48Al-2Cr alloys which produced with the similar compositions to those calculated. Calculations results show that addition of V and Cr alloying elements to binary TiAl can increase the yield strength of the alloy by increasing the lattice resistivity to motion of preferred dislocations. Also, addition of both the Cr and V alloying elements results in improving the ductility of TiAl alloys by reducing the resistance of the lattice to motion of the l/2< 110] ordinary dislocation and 1/2< 112] superdiclocation relative to the < 011] superdislocation which is in agreeing with the experimental results. Moreover, Results show that the Cr addition has more ductilizing effect on the binary TiAl compared to the V because of the fact that addition of Cr has a larger influence on nearing the tetragonal ratio to unityکلیدواژه ها
TiAl, deformation mechanisms, discrete variational-Xα method, mechanical behavior, alloy designingمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.