Two-Step Sintering of Dense Nanostuctured Hydroxyapatite/Titania composite
- سال انتشار: 1391
- محل انتشار: اولین کنفرانس بین المللی مواد پیشرفته
- کد COI اختصاصی: NAMIC01_071
- زبان مقاله: انگلیسی
- تعداد مشاهده: 2046
نویسندگان
Biomaterials Group, Department of Materials Engineering, Isfahan University of Technology, Isfahan, ۸۴۱۵۶۸۳۱۱۱, Iran
چکیده
Two-step sintering (TSS) has been applied to suppress the accelerated grain growth of Hydroxyapatite (HA) and Titania (TiO2) nanoparticles in the HA-TiO2 composites in the last sintering stage. Application of this method showed that the final grain size of HA-15wt.%TiO2 is maintained lower than 100nm, while through conventional sintering it reaches higher than 100nm. To find how important the temperatures at sintering steps might be, several TSS regimes were conducted. The results showed that the temperatures were critical at both sintering stages. The optimum regime consisted of heating the green bodies up to 1150˚C in the first step of sintering and then holding at 1050˚C for about 25h in the second step. This yielded the finest microstructure with no exaggeration in grain growth. The specimens prepared by optimum TSS regime resulted in no pernicious α-TCP phaseکلیدواژه ها
Nano structured Composites , Two Step Sintering , Hydroxyapatite , Scanning Electron Microscopyمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.