Synthesizing of nano-structure MgNi4Y alloy by mechanical milling and heat treatment
- سال انتشار: 1391
- محل انتشار: اولین کنفرانس بین المللی مواد پیشرفته
- کد COI اختصاصی: NAMIC01_064
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1569
نویسندگان
School of metallurgy and materials engineering, College of Engineering, University of Tehran, Tehran, ۱۴۳۹۹-۵۷۱۳۱, Iran
School of metallurgy and materials engineering, College of Engineering, University of Tehran, Tehran, ۱۴۳۹۹-۵۷۱۳۱, Iran
چکیده
In this study, an attempt was made to synthesize the Mg Ni4Y catalyst from pure Ni, Mg and Y elemental powders by mechanical milling and combination of mechanical milling and heat treatment methods. In this regard, powders of elements were ball milled at different conditions and then heat treated at 600ºC for 4 hour. X-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) methods were used to evaluate the characteristics of the milled mixtures. It was found from the results of XRD analysis that by increasing the ball milling time from 5 to 25 hours, the crystallite size of Nickel decreased from 16 to 4 nm and lattice strain increased from 0.05% to 4.19%, but ternary intermetallic was not observed after milling. XRD patterns showed that nano-structure MgNi4Y was formed after heat treatment. SEM micrographs of 25 hours milled samples revealed nano-size particles and agglomerates of Mg Ni4Y ternary intermetallic alloyکلیدواژه ها
Ball mill, Hydrogen storage, Nano-structure, MgNi4Y compoundمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.