High temperature oxidation behavior of graphite coated by dual layer of nano-SiC/SiC
- سال انتشار: 1391
- محل انتشار: اولین کنفرانس بین المللی مواد پیشرفته
- کد COI اختصاصی: NAMIC01_052
- زبان مقاله: انگلیسی
- تعداد مشاهده: 2022
نویسندگان
Faculty of Materials and Manufacturing Technology, MUT University, Tehran, Iran
Materials Engineering Department, Iran University of Science & Technology, Tehran, Iran
چکیده
In this research, a dual-layer coating was used to improve high temperature oxidation resistance of graphite substrate. For first layer, silicon carbide was applied by pack cementation method. Powder pack consisted of Si, SiC and Al2O3 and heat-treated at 1650°C in an argon atmosphere. SEM and XRD characterizations confirmed formation of SiC diffusion coating with about 500 μm including compositionally gradient of C and Si elements. Electrophoretic deposition (EPD) was used to deposit nano SiC (SiCn) as second layer. Thickness of second layer of SiCn in corresponded optimal situation was 50μm. Samples with single and dual layers were investigated in oxidation test at 1400°C. Results showed that an extreme increase was occurred in oxidation resistance after application of second layer of nano SiC. Weight loss value for single layer coating of SiC and dual layer coating of SiCn/SiC after oxidation test for 28h at 1400°C were 20 wt.% and 1 wt.%, respectivelyکلیدواژه ها
Oxidation, Coating, Nano SiC, Pack Cementation, Electrophoretic Depositionمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.