Effect of austenitic stainless steel cladding on the high-temperature oxidation resistance of ferritic ۲.۲۵Cr-۱Mo (Grade ۲۲) steel using the SMAW process

  • سال انتشار: 1400
  • محل انتشار: فصلنامه کامپوزیت ها و ترکیبات، دوره: 3، شماره: 7
  • کد COI اختصاصی: JR_JRCC-3-7_006
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 202
دانلود فایل این مقاله

نویسندگان

Hassan Jafarikhorami

Department of Materials, Science and Research Branch, Islamic Azad University, Tehran, Iran

چکیده

The high-temperature oxidation resistance of low alloy steel affected by the cladding of austenitic stainless steel has been investigated in this study. For this purpose, Shielded Metal Arc Welding (SMAW) technique was used to prepare a proper layer of AISI۳۴۷ on the surface of ferritic steels. The microstructure and morphology properties of the alloys were examined using transmission electron microscopy (TEM), scanning electron microscopy (SEM), and Energy Dispersive X-Ray Analysis (EDX) techniques. Results demonstrated that the construction of oxide shells on the surface of non-modified ferritic steel was responsible for its low resistance in contrast to the oxidation at high-temperature conditions. The oxidation screening of coated and uncoated samples with tuning time at constant temperature showed the increased oxidizing intensity of both materials. Conversely, with tuning temperature from ۸۵۰ to ۹۵۰ oC at a constant time, an abnormal increase was observed in oxidation intensity. The corresponding kPs of the uncoated sample was determinate ۱.۲۷۷۰۸×۱۰-۸, ۳.۲۶۷×۱۰-۸, and the corresponding kPs of coated material was determinate ۵۴.۵×۱۰-۱۰, ۶.۶×۱۰-۱۰. The performed investigation proved that the formation of oxidized compact needle microstructures in the resulting alloy is the reason for the extraordinarily oxidizing resistance of austenitic stainless steel.

کلیدواژه ها

Ferritic steels, Cr-Mo steel, SMAW technique, austenitic steel, Corrosion resistance, Oxidation

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.