Joining of Ti-۶AL-۴V to AISI ۳۰۴ Stainless Steel using Laser Spot Welding with Circular Technique
- سال انتشار: 1401
- محل انتشار: مجله مواد دوستدار محیط، دوره: 6، شماره: 1
- کد COI اختصاصی: JR_JEFM-6-1_007
- زبان مقاله: انگلیسی
- تعداد مشاهده: 137
نویسندگان
Department of Materials Engineering, Karaj Branch, Islamic Azad University, Karaj, Iran.
Department of Materials Engineering, Karaj Branch, Islamic Azad University, Karaj, Iran.
Advanced Materials Engineering Research Center,Karaj Branch, Islamic Azad University ,Karaj, Iran
Department of Mechanical Engineering, Technical and Vocational University (TVU), Tehran, Iran
چکیده
In this research, dissimilar laser spot welding of the Ti-۶Al-۴V and AISI ۳۰۴ (stainless steel) was investigated. The joining of ۰.۷ and ۰.۵ mm thickness plates with using a copper interlayer of ۰.۲ and ۰.۳ mm in thickness was performed by LSW. A ۴۰۰-W Nd: YAG laser pulse welding machine was used to obtain coaxial spot welds of ۴ mm in diameter with circular technique. Visual inspection and metallographic examination were used for all samples. If no crack was identified, micro-Vickers hardness test, tensile test, and scanning electron microscopy (SEM) were performed on the samples. The result indicated that with a copper interlayer and ۱۰.۷ J heat input on peak power of ۱.۵ kW, welding frequency ۱۵ Hz, and welding time of ۷ ms, leading to an ultimate strength of ۱۶۰ MPa. In addition the result indicated that applying the circular technique by creating adjacent spot welds can produce a good joint.کلیدواژه ها
laser spot welding, Ti-۶Al-۴V, AISI ۳۰۴, Circular Techniqueاطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.