Investigation of bond strength of AL۵۰۸۳/Polyurethane/AL۵۰۸۳ (APA)laminates and comparison of their mechanical properties with monolithicaluminium sheets
- سال انتشار: 1401
- محل انتشار: دومین کنفرانس بین المللی کاربرد مواد و ساخت پیشرفته در صنایع
- کد COI اختصاصی: IAAMM02_045
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1301
نویسندگان
Department of material science and engineering, Sharif University of technology;
Department of material science and engineering, Sharif University of technology;
Department of material science and engineering, Sharif University of technology;
چکیده
Metal/polymer/metal three-layer composites have exceptional properties such as excellent formability,improved mechanical properties, and special toughness. The use of these composite sheets is,however, limited due to the low bond strength between the metal skins and the polymeric core. In thisstudy, Aluminum۵۰۸۳/Polyurethane/Aluminum۵۰۸۳ three-layered sandwich sheets were produced byDirect Roll Bonding (without adhesive), through the cold rolling process. The influence of rollingspeed and thickness reduction on the bond strength of the sandwich sheet was studied. T-Peel anddouble-notch shear tests were performed to determine the normal and shear bond strength oflaminates. The results show that the highest bond strength was obtained at rolling speed and thicknessreduction of ۲۵rpm (round per minute) and ۳۰%, respectively. The mechanical properties of thelaminate sheet with most bonding strength were also obtained by Uniaxial Tensile test and comparedwith the monolithic aluminum sheets. Even though yield and ultimate strengths of the laminate werelower than the aluminum skin sheet, the total elongation of the three-layered laminate was higher thanthe monolithic skin sheet.کلیدواژه ها
Sandwich Laminates, Direct Roll Bonding, AL۵۰۸۳, Polyurethane Thermoplastic, Mechanicalpropertiesمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.