Synthesis and nano structural study on TiO۲-NiO-SiO۲ composite
- سال انتشار: 1393
- محل انتشار: مجله بین المللی ابعاد نانو، دوره: 5، شماره: 2
- کد COI اختصاصی: JR_IJND-5-2_004
- زبان مقاله: انگلیسی
- تعداد مشاهده: 150
نویسندگان
Department of Engineering, Tonekabon branch, Islamic Azad University, Tonekabon, Iran
چکیده
We report on the synthesis, morphology, chemically and structurally of TiO۲-NiO-SiO۲ nanostructure. The TiO۲-NiO-SiO۲ nanostructure was synthesized by a method based on the sol-gel method, by the simultaneous gelation of all cations. The coatings were deposited on dried soda-lime glass slides by spin coating. Composite powders and coating on glass have been characterized by XRD, SEM, EDAX, and FTIR. X-ray diffraction showed the formation of nano crystalline, anatase, TiO, NiO and NiTiO۳ phases. Scanning electron microscopy revealed that nanostructure formed by increasing the calcinations temperatures. EDX spectroscopy confirmed the composition of the ternary powders and coating, which were formed during the gelation process. The effects of chemical compositions and calcinations temperature on the surface topography and the crystallization of phases were studied. The activation energy (E) of nanoparticles formation during thermal treatment was calculated.کلیدواژه ها
nanostructure, Poly-component, TiO۲-NiO-SiO۲, Activation Energy, Sol-gel Methodاطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.