Electromagnetic absorption and structural properties of SrFe۱۱.۹۸Mg۰.۱Sn۰.۱O۱۹/BaTiO۳ nanocomposites
- سال انتشار: 1398
- محل انتشار: مجله بین المللی ابعاد نانو، دوره: 10، شماره: 3
- کد COI اختصاصی: JR_IJND-10-3_008
- زبان مقاله: انگلیسی
- تعداد مشاهده: 98
نویسندگان
Department of Chemistry, Tehran North Branch, Islamic Azad University, Tehran, Iran.
Department of Chemistry, Tehran North Branch, Islamic Azad University, Tehran, Iran.
Department of Chemistry, Yadegar-e-Imam Khomeini (RAH) Shahre Rey Branch, Islamic Azad University, Tehran, Iran.
Department of Chemistry, Tehran North Branch, Islamic Azad University, Tehran, Iran.
Department of chemistry, Science and Research Branch, Islamic Azad University, Tehran, Iran.
چکیده
In this research, first, nanoparticles of SrFe۱۱.۹۸Mg۰.۱Sn۰.۱O۱۹ hexaferrite was synthesized via sol-gel auto-combustion process and then the nanocomposites of hexagonal ferrites/perovskite with the amounts of SrFe۱۱.۹۸Mg۰.۱Sn۰.۱O۱۹/BaTiO۳ (۵۰/۵۰, ۴۰/۶۰, ۷۰/۳۰ w/w) was prepared by the ball-milling method. Fourier transform infrared (FTIR) spectrums of SrFe۱۱.۹۸Mg۰.۱Sn۰.۱O۱۹,was shown that the bands at about ۴۰۰ and ۵۰۰ cm-۱ proved the formation of nano hexagonal ferrites. On the FTIR spectrum of nanocomposites, the Ti-O bond of perovskite appeared. X-ray diffraction (XRD) analysis was confirmed the formation of hexaferrite and perovskite phase of BaTiO۳. Field emission electron microscopy (FESEM) pictures have represented the formation of hexagonal nanoparticles and sphere shape of BaTiO۳. Vibrating sample magnetometer (VSM) hysteresis loop was revealed that SrFe۱۱.۹۸Mg۰.۱Sn۰.۱O۱۹ belonged to the soft magnetic materials due to the ۶۰۴.۴۵Oe coercivity. By formation of nanocomposites, the coercivity was increased up to ۱۵۰۰ Oe. Vector network analyzer (VNA) analysis was revealed the maximum absorption of -۱۶.۴ db at ۱۱.۵ GHz frequency for SrFe۱۱.۹۸Mg۰.۱Sn۰.۱O۱۹/BaTiO۳ (۶۰/۴۰) nanocomposite sample.کلیدواژه ها
Ball- milling, Coercivity, Hexaferrite, Perovskite, Vector network analyzerاطلاعات بیشتر در مورد COI