The effect of partial Nb doping on magnetic and electrical behavior of Y-۱۲۳ superconductors with Nano CuO
- سال انتشار: 1400
- محل انتشار: مجله پژوهش فیزیک ایران، دوره: 21، شماره: 3
- کد COI اختصاصی: JR_PSI-21-3_007
- زبان مقاله: فارسی
- تعداد مشاهده: 137
نویسندگان
استاد-دانشگاه ارومیه
چکیده
We have investigated the effect of Niobium and Nano CuO (۴۰ nm) dopingY۱-xNbxBa۲Cu۳O۷-∂ compounds with ۰.۰۰ ≤ x ≤ ۰.۰۵ wt. %, prepared by the conventional solid-state method by means of XRD, SEM, R(T) and magnetic loops (MH) measurements. The critical current densities, Jc as a function of temperature have been calculated using the critical state model from the hysteresis loops up to ۱ kG at the temperature range of ۱۰-۶۰ K. Magnetic flux pinning, Fp of samples was calculated by using Lorentz force. The temperature dependence of the electrical resistivity measurement curves indicated that the sample with x=۰.۰۱ wt.% has a high transition temperature, Tc. XRD analysis shows a shorter c axis lattice parameter and higher orthoromthcity than the pure Y-۱۲۳ and other Nb-doped samples. It was also found from Jc and Fp measurement, that the ۰.۰۱ wt.% Nb substation for the Y on YBCO superconductor improves the Jc and Fp.کلیدواژه ها
high-Tc superconductors, x-ray, Critical current density (Jc), Flux pinning (Fp)اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.