Predicting the Quantity and Type of Intermetallic Phases in Aluminum – Steel Dissimilar Joints Produced by Zinc Interlayer
- سال انتشار: 1400
- محل انتشار: چهارمین کنفرانس بین المللی جوشکاری و آزمایش های غیرمخرب و بیست و دومین کنفرانس ملی جوش و بازرسی و یازدهمین کنفرانس ملی آزمایش های غیرمخرب
- کد COI اختصاصی: INCWI22_026
- زبان مقاله: انگلیسی
- تعداد مشاهده: 350
نویسندگان
PhD Student, Department of Materials and Metallurgical Engineering, Amirkabir University of Technology
Assistant Professor, Department of Materials and Metallurgical Engineering, Amirkabir University of Technology
Associate Professor, Department of Materials and Metallurgical Engineering, Amirkabir University of Technology
چکیده
In this study, the formation of brittle intermetallic compounds in over-lap joints of ۱۱۰۰ aluminum and low-carbon galvanized steel made by Gas - Tungsten arc welding method was investigated. The welding process was simulated by finite-element method and temperature histories during the welding process were derived from it. The Gibbs free energy of Fe-Al and Fe-Zn intermetallic phases were calculated and their formation was predicted by means of thermodynamic modeling. The growth behavior of IMCs at the interface of the joint was studied through optical and scanning electron microscopy and energy-dispersive X-ray spectroscopy. A relation was provided to predict the thickness of the formed compounds at the interface. The modeling results revealed the formation of FeAl۳ and Fe۲Al۵ compounds, which were consistent with the experimental results. Studying the compounds growth behavior proved that the zinc coating on galvanized steel can act as an interlayer to delay and limit the growth of intermetallic compounds at the interface. The thickness of the intermetallic layer in samples welded with ۱۰۰A and ۱۱۰A currents were ۶.۲ and ۱۰.۲ μm, respectively, which was reduced by an average of ۷۰% compared to the conditions without the presence of the zinc interlayer.کلیدواژه ها
Finite element method, GTAW, Thermodynamic modeling, Growth kinetics, Intermetallic compoundsمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.