Synthesis of the Single-Phase Bismuth Ferrite (BiFeO۳) Nanoparticle and Investigation of Their Structural, Magnetic, Optical and Photocatalytic Properties
عنوان مقاله: Synthesis of the Single-Phase Bismuth Ferrite (BiFeO۳) Nanoparticle and Investigation of Their Structural, Magnetic, Optical and Photocatalytic Properties
شناسه ملی مقاله: JR_AJCS-5-1_005
منتشر شده در در سال 1401
شناسه ملی مقاله: JR_AJCS-5-1_005
منتشر شده در در سال 1401
مشخصات نویسندگان مقاله:
Seyed Ebrahim Mousavi Ghahfarokhi - Department of Physics, Faculty of Science, Shahid Chamran University of Ahvaz, Ahvaz, Iran
Khadijeh Helfi - Department of Physics, Faculty of Science, Shahid Chamran University of Ahvaz, Ahvaz, Iran
Morteza Zargar Shoushtari - Department of Physics, Faculty of Science, Shahid Chamran University of Ahvaz, Ahvaz, Iran
خلاصه مقاله:
Seyed Ebrahim Mousavi Ghahfarokhi - Department of Physics, Faculty of Science, Shahid Chamran University of Ahvaz, Ahvaz, Iran
Khadijeh Helfi - Department of Physics, Faculty of Science, Shahid Chamran University of Ahvaz, Ahvaz, Iran
Morteza Zargar Shoushtari - Department of Physics, Faculty of Science, Shahid Chamran University of Ahvaz, Ahvaz, Iran
In this study, single-phase bismuth ferrite (BiFeO۳) was synthesized using hydrothermal method. The effect of KOH concentration and temperature during the reaction on morphology, particle size, and phase formation was investigated. Then, the structural properties of the samples were assessed using X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), Fourier transform-infrared spectroscopy (FT-IR), and vibrating sample magnetometer (VSM) analysis. XRD analysis results revealed that the samples were fabricated in distorted rhombohedral perovskite structure with R۳C space group. Also, BiFeO۳ (BFO) was formed in a single-phase at ۲۲۰ °C and ۴M concentration of KOH. The magnetic properties of the optimal sample were determined by VSM analysis and very weak magnetic properties were observed in pure nanoparticles. Also, the optical properties and photocatalytic properties of the optimal sample were investigated by UV-visible and Photoluminescence (PL) analysis. The optical gap of BFO was recorded by ۲.۸ and its photocatalytic properties were investigated at three different pHs (۲, ۶, and ۱۰) at a concentration of ۲۰ ppm Congo red. The results demonstrated that BFO nanoparticles nearly destroyed dye structure after ۱۲۰ min at pH = ۲.
کلمات کلیدی: Bismuth ferrite, Hydrothermal method, Structural properties, Magnetic properties, photocatalytic properties