Preparation of Cobalt Oxide/Zinc Oxide Nanocomposite
- سال انتشار: 1389
- محل انتشار: ماهنامه بین المللی مهندسی، دوره: 23، شماره: 2
- کد COI اختصاصی: JR_IJE-23-2_004
- زبان مقاله: انگلیسی
- تعداد مشاهده: 153
نویسندگان
materials department, KNTU
Nanotechnology and Advanced Materials Department, Material and Energy Research Center(MERC)
Research Center of Advanced Materials, Merc
Applied Science, RMIT - RMIT University
چکیده
Cobalt Oxide/ Zinc Oxide nanocomposite was synthesized by dropwise addition ofCo(NO)۳.۶H۲O and Zn(NO۳)۲.۴H۲O solutions to KOH solution at different temperatures followed bycalcination at ۳۰۰ºC for ۴ h. The morphology and structure of nanoparticles and the influence oftemperature on particle size were studied using scanning electron microscopy (SEM) and X-RayDiffraction (XRD). Minimum particle size was obtained before calcination at ۷۰ºC. In addition, thespherical, semispherical and flake-shaped nanoparticles were observed at ambient temperature. Onthe other hand, Co(OH)۲ was transformed to Co۳O۴, ZnO flakes were eliminated, and particle sizechanged during calcination. Synthesized samples at ۵۰ºC and ۷۰ºC showed an increase size aftercalcinations; however, elimination of flakes during calcination caused particle size reduction forsynthesized sample at ambient temperature.کلیدواژه ها
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.