Effect of Composition on the Recrystallization Behavior of if Steels During Simulated Hot Strip Rolling
عنوان مقاله: Effect of Composition on the Recrystallization Behavior of if Steels During Simulated Hot Strip Rolling
شناسه ملی مقاله: JR_IJE-5-1_006
منتشر شده در در سال 1371
شناسه ملی مقاله: JR_IJE-5-1_006
منتشر شده در در سال 1371
مشخصات نویسندگان مقاله:
J. J. Jonas - Materials Engineering, McGill University
A. Najafizadeh - Materials Engineering, Isfahan University of Technology
خلاصه مقاله:
J. J. Jonas - Materials Engineering, McGill University
A. Najafizadeh - Materials Engineering, Isfahan University of Technology
Flow curves are generated in muti-pass torsion tests for a titanium stabilized and a niobium stabilized IF steel. Two types of test schedule are used, one based on plate rolling and the other approximating strip rolling. The purpose of the former is to define the three critical temperatures of steel rolling. The strip schedules are varied in order to investigate the influence of increasing the total finishing strain (from ۲.۱ to ۳.۲) and lowering the first finishing pass temperature (from ۹۹۰ to ۹۳۰°C) on microstructural evolution in these steels. All the tests are carried out at a strain rate of ۲s-۱. Under hot strip rolling conditions, static recrystallization is responsible for the high degree of interpass softening. During the final passes, dynamic recrystallization occurs to a degree that depends on the composition of the steel, the total finishing strain and the temperature. Subjected to the same strip rolling schedule, the niobium stabilized steel has a finer ferrite grain size than the IF steel stabilized with titanium.