Enhanced Dielectric Properties in Bismuth Titanate Ceramics with CuO Sintering Aid
- سال انتشار: 1400
- محل انتشار: دهمین کنفرانس بین المللی مهندسی مواد و متالورژی (iMat۲۰۲۱)
- کد COI اختصاصی: IMES15_151
- زبان مقاله: انگلیسی
- تعداد مشاهده: 384
نویسندگان
Assistant Professor, Department of Materials Science and Engineering, School of Engineering, Shahrekord University, Shahrekord, Iran
چکیده
Bismuth titanate (Bi۴Ti۳O۱۲) is a prominent member of bismuth oxide layer structure ferroelectrics. Bi۴Ti۳O۱۲ is a potential candidate for high-temperature applications due to its high Curie temperature. In this study, Bi۴Ti۳O۱۲ ceramic was synthesized using the solid state reaction method. The effects of ۰.۵ mol% CuO as sintering aid on the microstructure and dielectric properties were investigated. It was found that the use of CuO led to the enhanced densification of Bi۴Ti۳O۱۲ ceramic and obtained high density ceramic. The random orientation of grains was reduced and the grain shape change from plate-like to needle-shape in the sample including CuO. The results indicated that the addition of CuO increased the dielectric constant and decreased the dielectric loss of BIT ceramic.کلیدواژه ها
Bismuth titanate, CuO, Sintering aid, Dielectric properties, Microstructureمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.