Ali Mohebbi - Department of Chemical Engineering, Faculty of Engineering, Shahid Bahonar University of Kerman, Kerman, Iran
Mahboobeh Taheri - Department of Chemical Engineering, Faculty of Engineering, Shahid Bahonar University of Kerman, Kerman, Iran
Hassan Hashemipour - Department of Chemical Engineering, Faculty of Engineering, Shahid Bahonar University of Kerman, Kerman, Iran
Ali Morad Rashidi - Research Institute of Petroleum Industry (RIPI), Tehran, Iran

    In this study, it was shown that how CO۲ and H۲S were removed from a natural gas stream, using a nanofluid containing nanoporous graphene in Diehanolamine (DEA). Before running the experiments, the appropriate values were chosen for the nanosheet dosage and the liquid and gas flow rates in the absorption experiments, which were performed in a laboratory scale wetted wall column. In the experiments, the nanosheet concentration ranged from ۰.۰۰۵ to ۰.۵ wt %.The surfactants and ultrasonic treatment  were used to prepare stable nanofluids. It was indicated that using nanoporous graphene in DEA significantly affects on CO۲ and H۲S absorption in comparison to DEA. The absolute zeta potential values of nanofluids were greater than +۳۵ mV. The effect of different parameters including nanosheet concentration as well as the CO۲ and H۲S concentration, in the feed gas stream (two different samples) on simultaneous absorption of H۲S and CO۲ from CO۲-H۲S-CH۴ gas mixture was studied. In the case of using sample #۱, (i.e. Feed gas mixture composition: % H۲S and ۳% CO۲ in balance of CH۴), an improvement in CO۲ absorption to ۳۹% and H۲S absorption to ۹% was observed at ۰.۱ wt% of nanoporous graphene/DEA nanofluids.

Nanofluid, Wetted Wall Column, Hydrogen sulfide, Carbon dioxide, Diethanolamine, Nanoporous Graphene