chemical and Morphological influence of SALT fog aging on silicon insulators
- سال انتشار: 1390
- محل انتشار: بیست و ششمین کنفرانس بین المللی برق
- کد COI اختصاصی: PSC26_005
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1817
نویسندگان
Niroo Research Institute- Tehran- Iran
Niroo Research Institute, Tehran, Iran
Taban Niroo Company, Shiraz, Iran
چکیده
This work investigates on morphological and chemical characteristics of the surface of silicon insulators under aging conditions. For this purpose, a 500 hour salt-fog test was carried out on 24 KV insulators according to IEC 61109. FT-IR results showed that the intensity of Si-CH3 bond increased in the (SEM) was employed to monitor the morphological characteristics of the insulator after the test. SEM micrographs showed that the roughness of the sample increased under aging conditions. In order to investigate fillers’ concentration of the insulator before and after aging, Scanning Electron Al/Si of the virgin sample is higher than that of the aged one. It is due to deficiency of Al and Si fillers.کلیدواژه ها
Salt Fog, Morphological, Aging, Silicone, Insulatorمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.