Studying the Stability of Melting and Solidification Behavior of Phase Change Material
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 171
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_APRIE-4-3_005
تاریخ نمایه سازی: 2 دی 1400
چکیده مقاله:
Experimental analysis of thermal properties of phase change material was conducted using DCS and TG apparatus. Moderate rang of temperature of phase change material was selected and experimentally investigated. Measurement of melting and solidification temperature at several heating rate are carried out. Furthermore, the stability and thermal decomposition of the selected phase change material are also investigated. Experiment demonstrates clearly the phase change material effect in melting and solidification. The lab test with DSC and TG proves that the catalogue data of the Plus ICE H۱۹۰ PCM is reasonable to be used for thermal storage devices with great deal of consistency. In general, results showed that the utilization of phase change material in thermal storage is feasible to store and extract heat at constant temperature in the range between ۱۷۰oC to ۲۰۰oC which has many applications in engineering and industry.
کلیدواژه ها:
نویسندگان
Abdullah. N. Olimat
Department of Fire Safety Engineering, Prince Hussein Bin Abdullah II Academy of Civil Protection, Jordan.
Ahmed Al-Salaymeh
Department of Mechanical Engineering, University of Jordan, Jordan.
Ayman Al-Maaitah
Department of Mechanical Engineering, Mu&#۰۳۹;tah University, Jordan.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :