Enhancement of E-glass fiber/epoxy composite bending performance via graphene addition
- سال انتشار: 1399
- محل انتشار: فصلنامه علوم و فناوری ذرات، دوره: 6، شماره: 2
- کد COI اختصاصی: JR_JPST-6-2_001
- زبان مقاله: انگلیسی
- تعداد مشاهده: 170
نویسندگان
Department of Mechanical Engineering, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran
Department of Materials Engineering, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran
چکیده
This paper presents an experimental investigation using graphene nanoplatelets (GnPs) to enhance the bending performance of E-glass fiber/epoxy composites. Each specimen was prepared with two layers of E-glass chopped strand mat via the hand lay-up technique and using various contents of GnPs in the matrix (۰.۱, ۰.۲, ۰.۳, ۰.۴ and ۰.۵ wt%). Mechanical and ultrasonic stirring methods were employed to disperse the GnPs in the matrix. The obtained results demonstrated that the highest increases of ۲۳% and ۲۶% in the flexural strength and modulus, respectively, were observed for the composite containing ۰.۴ wt% GnPs. With the incorporation of ۰.۱ wt% GnPs, the flexural failure strain of the composite was enhanced by ۱۶% compared to the control composite. The evaluation of the fractured surfaces clearly demonstrated that the interface between the glass fiber and polymeric matrix was improved when GnPs were added into the matrix.کلیدواژه ها
Fiber-reinforced composite, Graphene nanoplatelets, Bending performance, fracture surfaceاطلاعات بیشتر در مورد COI