studies on Rheolgical Behavir and Processing of Mosi2 Heating Element
محل انتشار: ششمین کنفرانس ملی مهندسی ساخت و تولید
سال انتشار: 1382
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,254
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICME06_092
تاریخ نمایه سازی: 7 اسفند 1390
چکیده مقاله:
Rheology and processing of MOSi2 for injection molding of cylindrical heating elements were studied MoSi2 production through colloidal processing requires a good estimtate of the critical powder volume content CPVC in the present research the powder mic consisted of a commercial MoSi2 powder and a binder composed of paraffin bee's wax and polyethylene viscosity of the mix was measured by an RVT viscometer at different powder contents and the CPVC was calculated to be~60-65% at 130 C and shear rated of 2.5 to 20/s it was concluded that CPVC depends on the speed shear rate and the temperatur of mixing it increased with these parameters the inject molded samples were sintered at 1300 C for 2 hours and their microstructures were observed by SEM and analyzed by EDS
نویسندگان
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :