Thermal Degradation of HDPE/Caco3 Nanocomposites: Effect of Content of Nano and MFI

سال انتشار: 1390
محل انتشار: کنفرانس بین المللی فرآورش پلیمرها
کد COI اختصاصی: PPSRC2011_217
زبان مقاله: انگلیسی
تعداد مشاهده: 1421

نویسندگان

Department of Chemical Engineering Farahan branch, Islamic Azad University Farahan, Iran

چکیده

In the present study different series of high-density polyethylene (HDPE) nanocomposites, containing 1, 3 and 5 wt.% of carbonate calcium (CaCo3) nanoparticles and HDPE with different MFI were prepared by melt-mixing on a internal mixer(plasticorder PL2000 Brabender). From TGA analysis, the decomposition temperature of nanocomposites with surface treatment of nano and HDPE with high MFI increased and has higher resistance to thermal degradation. According to the SEM micrographs, it was found that a much better dispersion of nano CaCo3 in samples with higher MFI also according to the SEM and TEM measurement, was found that nano CaCo3 with surface treatment has better dispersion compared nano without surface treatment. The properties of HDPE and its nanocomposite were investigated through differential scanning calorimetery (DSC) test. The results of DSC tests showed that the addition of nano-sized calcium carbonate to HDPE caused to increase the heat capacity and crystallinity.

کلیدواژه ها

HDPE, Nano CaCo3, Thermal degradation, Nanocomposite

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.