Application of Hamedan's andalusite for the manufacturing of cordierite-mullite refractory materials
عنوان مقاله: Application of Hamedan's andalusite for the manufacturing of cordierite-mullite refractory materials
شناسه ملی مقاله: JR_JGEO-3-2_004
منتشر شده در در سال 1386
شناسه ملی مقاله: JR_JGEO-3-2_004
منتشر شده در در سال 1386
مشخصات نویسندگان مقاله:
Seyad Hossein Badiee - Faculty of Engineering, Islamic Azad University - Maybod Branch, Maybod, Iran
Sasan Otroj - Faculty of Engineering, Shahrekord University, Shahrekord, Iran
خلاصه مقاله:
Seyad Hossein Badiee - Faculty of Engineering, Islamic Azad University - Maybod Branch, Maybod, Iran
Sasan Otroj - Faculty of Engineering, Shahrekord University, Shahrekord, Iran
In this research, andalusite of Hamedan and other Iranian raw materials such as talc, kaolin, calcined alumina and magnesium oxide have been used for manufacturing of cordierite-mullite refractory materials. Different formulations were considered according to the chemical composition of raw materials. Then, raw materials were mixed, uniaxially pressed and after drying fired at different temperatures. Phase analysis (by XRD) and thermal expansion coefficient of fired samples were investigated. The results showed that Hamedan's andalusite can be used for the manufacturing of cordierite-mullite refractory materials. The optimum firing temperature range for cordierite and mullite phase formation is ۱۳۰۰-۱۳۵۰ ºC for ۱۰ hrs.
کلمات کلیدی: Cordierite, Mullite, Andalusite, Phase analysis, Thermal expansion