The Effect of Weight Fraction, Silanization and Size of Fillers on the Mechanical Properties of an Experimental SiO۲ Dental Composite

سال انتشار: 1397
محل انتشار: دوفصلنامه ارتودنسی ایران، دوره: 13، شماره: 1
کد COI اختصاصی: JR_ORTHO-13-1_007
زبان مقاله: انگلیسی
تعداد مشاهده: 215

نویسندگان

Polymer research Lab., School of Chemical Engineering, Iran University of Science and Technology, Tehran, Iran

چکیده

Background This research studied mechanical properties of silica-based nanocomposite as a strong restorative material through flexural test method. Objectives The purpose of this study was to evaluate the effect of weight fraction, silanization and filler size on the flexural properties of silica-based dental nanocomposite. Methods The prepared composites were made of light-cured copolymer based on Bisphenol A glycolmethacrylate (Bis-GMA) and Triethylene glycoldimethacrylate (TEGDMA) at proportion of ۵۰:۵۰ which reinforced by silica filler. The effect of silanization and weight fraction of the filler was studied with samples containing ۱۰ wt% (n (۱۰)), ۲۰ wt% (n (۲۰)) and ۳۰ wt% (n (۳۰)) nanosilica filler. Samples silanized with (γ-MPS) were also tested. Flexural properties were evaluated with Three-Point Bending test. Flexural strength of the nano SiO۲ based composites were also compared to micro silica glass composites. Flexural data were analyzed with one-way analysis of the variance. Results The sample with ۱۰ wt% (n (۱۰)) had equal strength as the sample with ۳۰ wt% (n (۳۰)) nanosilica filler. Modulus of the sample n (۳۰) was higher than the other samples, but its toughness was significantly lower. Silanization had not expected positive effect on the flexural properties. Conclusions Adding low amount of nanosilica improved mechanical properties of the resin composite. Silanization of the particles enhanced workability of the paste, but mechanical properties decreased significantly. Reduction in the size of the filler to nano scale caused better flexural strength in comparison to micro glass silica composites.

کلیدواژه ها

Nanosilica Composite, Flexural Strength, Modulus, Salinization

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.